Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ISO 1183 | 1.45 | g/cm³ |
| Shrinkage rate | 横向流量 | 内部方法 | 0.30 到 0.70 | % |
| Shrinkage rate | 流量 | 内部方法 | 0.10 到 0.40 | % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.020 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO 527-2 | 10500 | Mpa |
| tensile strength | 断裂 | ISO 527-2 | 110 | Mpa |
| elongation | 断裂 | ISO 527-2 | 1.5 | % |
| Bending modulus | | ISO 178 | 10300 | Mpa |
| bending strength | | ISO 178 | 170 | Mpa |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 9.0 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 28 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 8.0 | kJ/m² |
| Cantilever beam without notch impact strength | 23°C | ISO 180 | 26 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 265 | °C |
| Hot deformation temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 230 | °C |
| Linear coefficient of thermal expansion | 流动 : -30 到 30°C | TMA | 1.9E-5 | cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 : -30 到 30°C | TMA | 4.2E-5 | cm/cm/°C |
| RTI Elec | | UL 746 | 130 | °C |
| RTI Imp | | UL 746 | 120 | °C |
| RTI | | UL 746 | 130 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | IEC 60093 | > 1.0E+16 | ohms·cm |
| Dielectric strength | | ASTM D149 | 35 | KV/mm |
| Dielectric constant | 1 MHz | IEC 60250 | 3.00 | |
| Dissipation factor | 1 MHz | IEC 60250 | 2.0E-3 | |
| Arc resistance | | ASTM D495 | PLC 6 | |
| Compared to the Leakage Tracking Index (CTI) of | | IEC 60112 | PLC 1 | |
| High arc combustion index (HAI) | 0.75 mm | UL 746 | PLC 0 | |
| High arc combustion index (HAI) | 1.5 mm | UL 746 | PLC 0 | |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 3 | |
| Hot wire ignition (HWI) | 0.75 mm | UL 746 | PLC 3 | |
| Hot wire ignition (HWI) | 1.5 mm | UL 746 | PLC 2 | |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| drying temperature | | | 120 | °C |
| drying time | | | 3.0 到 5.0 | hr |
| Processing (melt) temperature | | | 280 到 310 | °C |
| Mold temperature | | | 130 到 155 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | > 0.75 mm | UL 94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.