PC/ABS NH-1015 K25497 Samsung Cheil South Korea

Form：Granules | Grade：Flame retardant grade

Properties:

Chemical resistanceHigh rigidityThermal stabilityHigh impact resistance

Typical Applications:

Engineering accessoriesAutomotive Applications

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Engineering accessories \| Automotive Applications
Properties:	Chemical resistance \| High rigidity \| Thermal stability \| High impact resistance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	44	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	40	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning wire flammability index	1.0mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	775	°C
UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	2.0mm	UL 94	5VB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VA
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/50	2500	Mpa
tensile strength	Yield	ASTM D638	62.0	Mpa
	tensile strength	Yield	ISO 527-2/50	60.0	Mpa
	tensile strength	tensile strength	Break	ISO 527-2/50	48.0	Mpa
Bending modulus		ASTM D790	2400	Mpa
Bending modulus	Bending modulus		ISO 178	2450	Mpa
bending strength		ASTM D790	86.0	Mpa
bending strength	bending strength		ISO 178	88.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/B50	98.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	100	°C
RTI Elec	1.5mm	UL 746	90.0	°C
RTI Imp	1.5mm	UL 746	85.0	°C
RTI Str	1.5mm	UL 746	90.0	°C
Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	93.0	°C
	Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	98.0	°C
		Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	81.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	93.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220°C/10.0kg	ASTM D1238	23	g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ISO 1133	23	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
High arc combustion index	1.5mm	UL 746	PLC 3
Hot wire ignition	1.5mm	UL 746	PLC 2
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ISO 2039-2	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.