Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.70to2.03 |
| Apparent density | | g/cm³ | 0.68to0.95 |
| Water absorption rate | | % | 0.10to0.16 |
| Shrinkage rate | | mm/mm | 0.019-137.2E-3 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 51to110 |
| Barcol Hardness | | | 9.1to50 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | % | 24to47 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | % | 0.60to1.1 |
| compressive strength | | | 136.55to180.0 Mpa |
| yield | | | 41.24to55.72 Mpa |
| yield | | | 68.97to113.79 Mpa |
| Flexural modulus | | | 9310.34to18344.83 Mpa |
| Tensile modulus | | | 9586.21to20137.93 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 0.007to0.061 |
| Charpy Notched Impact Strength | | J/m | 0.008to0.010 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | | 4.20to6.15 |
| Dissipation Factor | | | 6.3E-3到0.028 |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 0 |
| Volume resistivity | | ohms·cm | 2.5E+14到6.6E+15 |
| arc resistance | | sec | 180to191 |
| dielectric strength | | V/mil | 260to380 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 258to260 |
| Linear coefficient of thermal expansion | | mm/mm/°C | 61.0E-5到101.6E-5 |
| Continuous use temperature | | °C | 165to222 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare