Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.40 g/cm³ |
| density | | ISO1183 | 1.40 g/cm³ |
| Water absorption rate | | ISO62 | 0.20 % |
| Moisture content | | ISO960 | <800 ppm |
| density | | ISO1183 | 1.40 g/cm³ |
| Water absorption rate | | ISO62 | 0.20 % |
| Moisture content | | ISO960 | <800 ppm |
| Water absorption rate | | ISO 62 | 0.20 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/5 | 16000 MPa |
| Tensile stress | | ISO527-2/5 | 120 MPa |
| Tensile modulus | | ISO527-2/5 | 16000 MPa |
| Tensile stress | | ISO527-2/5 | 120 MPa |
| Tensile modulus | | ISO 527-2/5 | 16000 MPa |
| Tensile stress | | ISO 527-2/5 | 120 MPa |
| Tensile strain | | ISO 527-2/5 | 1.5 % |
| | ISO 180/1U | 40 kJ/m² |
| | ISO 180/1U | 45 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 6.0 kJ/m² |
| Tensile strain | | ISO527-2/5 | 1.5 % |
| Tensile strain | | ISO527-2/5 | 1.5 % |
| Impact strength of cantilever beam gap | | ISO 180/1A | 7.0 kJ/m² |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/1A | 6.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 7.0 kJ/m² |
| | ISO180/1U | 40 kJ/m² |
| | ISO180/1U | 45 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 6.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 7.0 kJ/m² |
| | ISO180/1U | 40 kJ/m² |
| | ISO180/1U | 45 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC60093 | 1E+03 ohms·cm |
| Volume resistivity | | IEC60093 | 1E+03 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO11357 | 225 °C |
| melting temperature | | ISO11357 | 225 °C |
| melting temperature | | ISO 11357 | 225 °C |
| Electrical performance | | IEC 60093 | 1E+03 ohms·cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.