'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PBT/ASA S 4090 G2 BK BASF GERMANY
131
Form：Granules | Grade：Injection grade
Properties:
Low warpageDimensional stabilityFiller: Glass fiber reinffillerGlass fiber reinforced ma10%Filler by weight10%Filler by weight
Typical Applications:
Laptop caseShellEngineering accessoriesLaptop caseApplied in fields that require high performance leAs for the load-bearing parts in different industrShellEngineering accessoriesLaptop case
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Laptop case | Shell | Engineering accessories | Laptop case | Applied in fields that require high performance le | As for the load-bearing parts in different industr | Shell | Engineering accessories | Laptop case |
| Properties: | Low warpage | Dimensional stability | Filler: Glass fiber reinf | filler | Glass fiber reinforced ma | 10% | Filler by weight | 10% | Filler by weight |
Certificates
No Data...
Technical Data Sheet
| Other performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Fiberglass content | 20 | % | ||
| machinability | Test Condition | Test Method | Test Result | Test Unit |
| Mold temperature | 60-100 | °C | ||
| Melt Temperature | 250-270 | °C | ||
| Basic Performance | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | 0.4 | % | ||
| melt mass-flow rate | ISO 1133 | 20 | cm3/10min | |
| density | ISO 1183 | 1.39 | g/cm³ | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Ball Pressure Test | ISO 2039-1 | 153 | Mpa | |
| Charpy Notched Impact Strength | 7 | kJ/m² | ||
| Impact strength of simply supported beam without notch | 23 ℃ | 55 | kJ/m² | |
| bending strength | ISO 178 | 151 | Mpa | |
| elongation | Break | 2.5 | % | |
| tensile strength | ISO 527-1/-2 | 100 | Mpa | |
| Tensile modulus | ISO 527-1/-2 | 6900 | Mpa | |
| Tensile creep modulus | 1000Hr | ISO 899-1 | 3300 | Mpa |
| bending strength | 23°C | ISO 178 | 119 | Mpa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.0 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 37 | kJ/m² |
| -30°C | ISO 179/1eU | 24 | kJ/m² | |
| tensile strength | 23°C | ISO 527-2 | 75 | Mpa |
| Elongation at Break | 23°C | ISO 527-2 | 2.9 | % |
| Tensile modulus | 23°C | ISO 527-2 | 4500 | Mpa |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | ISO 11359-1/-2 | 0.4 | E-4/°C | |
| Hot deformation temperature | 1.80 MPa | 160 | °C | |
| Combustibility | UL 94 | HB | ||
| Hot deformation temperature | 0.45MPaUnannealed | ISO 75-2/Bf | 190 | °C |
| 1.80MPaUnannealed | ISO 75-2/Af | 105 | °C | |
| Melting temperature | ISO 11357-3 | 223 | °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 5.5E-05 | cm/cm/°C |
| thermal conductivity | DIN 52612 | 0.27 | W/m/K | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | Across Flow | 0.16 | % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.40 | % |
| 23°C,50RH | ISO 62 | 0.20 | % | |
| melt mass-flow rate | 275℃/2.16Kg | ISO 1133 | 35 | cm3/10min |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dissipation factor | 23°C | IEC 60250 | 0.021 | 1MHz |
| 23°C | IEC 60250 | 3.1E-03 | 100HZ | |
| Dielectric constant | 23°C | IEC 60250 | 3.40 | 1MHz |
| 23°C | IEC 60250 | 3.60 | 100HZ | |
| Dielectric strength | 1.50mm | IEC 60243-1 | 22 | KV/mm |
| Surface resistivity | IEC 60093 | 1E+14 | Ω.cm | |
| Volume resistivity | IEC 60093 | 1E+14 | Ω.cm | |
| flame retardancy | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | Allcolor | UL -94 | HB | 0.71mm |
| Allcolor | UL -94 | HB | 1.50mm | |
| Allcolor | UL -94 | HB | 3.00mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.