Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.36 g/cm³ |
| density | | ISO 11832 | 1360 kg/m³ |
| viscosity number | | ISO 307 | 130 cm³/g |
| viscosity number | | ISO 307 | 130 cm³/g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 220 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | <100 mm/min |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | ISO 12102 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 650 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Automotive Materials | | FMVSS302 | + |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | ISO 527-22 | 175 MPa |
| Tensile strain | | ISO 527-2 | 3.0 % |
| Tensile strain | Break | ISO 527-22 | 3.0 % |
| bending strength | | ISO 178 | 260 MPa |
| Tensile modulus | | ISO 527-2 | 9000 MPa |
| Tensile modulus | | ISO 527-22 | 9000 MPa |
| tensile strength | | ISO 527-2 | 175 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 12 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA2 | 12.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 70 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU2 | 70.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO 11357-3 | 260 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.