Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD4883 | 0.918 g/cm³ |
| melt mass-flow rate | | ISO1872-2 | 1.0 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 55 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | | ISO14782 | 8.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | Yield | ISO1872-2 | 9.00 MPa |
| Tensile strain | Break | ISO1872-2 | >430 % |
| Flexural modulus | | ISO1872-2 | 200 MPa |
| film | Test Condition | Test Method | Test Result |
|---|
| Film thickness - tested | | | 30 µm |
| Tensile modulus | | ISO527-3 | 190 MPa |
| Tensile modulus | | ISO527-3 | 220 MPa |
| Tensile stress | | ISO527-3 | 55.0 MPa |
| Tensile stress | | ISO527-3 | 40.0 MPa |
| elongation | | ISO527-3 | 550 % |
| elongation | | ISO527-3 | 850 % |
| Falling hammer impact | | ISO7765-1 | 120 g |
| Elmondov tear strength | | ISO6383-2 | 30 N |
| Elmondov tear strength | | ISO6383-2 | 160 N |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ISO974 | <-70.0 °C |
| vicat | | ISO306 | 102 °C |
| melting temperature | | ISO11357-3 | 122 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.