EVA ELEVATE™ EF529 USA Huamei Chemistry

Compare

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
gloss	45°,31.8μm,Blown Film	ASTM D2457	82
turbidity	31.8μm,Blown Film	ASTM D1003	3.6 %

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ASTM D1525	67.0 °C
Melting temperature		ASTM D3418	85.0 °C

Physical properties	Test Method	Test Result
density	ASTM D1505	0.940 g/cm³
melt mass-flow rate	ASTM D1238	2.5 g/10min
Vinyl acetate content		18.5 wt%

film	Test Condition	Test Method	Test Result
film thickness			32 µm
Secant modulus	1%Secant,MD:32μm,Blown Film	ASTM D882	42.1 MPa
Secant modulus	Secant modulus	1%Secant,TD:32μm,Blown Film	ASTM D882	50.3 MPa
tensile strength	MD:Break,32μm,Blown Film	ASTM D882	24.8 MPa
tensile strength	tensile strength	TD:Break,32μm,Blown Film	ASTM D882	24.1 MPa
elongation	MD:Break,32μm,Blown Film	ASTM D882	600 %
elongation	elongation	TD:Break,32μm,Blown Film	ASTM D882	800 %
Dart impact	32μm,Blown Film	ASTM D1709	290 g

Supplementary Information	Test Condition	Test Method	Test Result
BlownFilmMeltTemperature			<177 °C
Cast Film Melt Temperature			<204 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.