Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D-955 | 0.4-1.1 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D-570 | 0.10 % |
| density | | ASTM D-792 | 1.60 g/cm³ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Charpy impact strength | | ASTM D256/ISO 179 | 450 kg·cm/cm(J/M)ft·lb/in |
| Charpy impact strength | | ASTM D256/ISO 179 | 70 kg·cm/cm(J/M)ft·lb/in |
| elongation at break | | ASTM D638/ISO 527 | 2 % |
| tensile strength | | ASTM D638/ISO 527 | 115 kg/cm²(MPa)[Lb/in²] |
| Flexural modulus | | ASTM D790/ISO 178 | 9000 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 185 kg/cm²(MPa)[Lb/in²] |
| Izod notched impact strength | | ASTM D-256 | 70 J/m |
| Izod notched impact strength | | ASTM D-256 | 450 J/m |
| elongation | | ASTM D-638 | 2 % |
| Flexural modulus | | ASTM D-790 | 9000 Mpa |
| bending strength | | ASTM D-790 | 185 Mpa |
| tensile strength | | ASTM D-638 | 115 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTM D150/IEC 60250 | 3.5 |
| Volume resistivity | | ASTM D257/IEC 60093 | 1016 Ω.cm |
| Dielectric loss | | ASTM D-150 | 0.02 |
| dielectric strength | | ASTM D-149 | 21 KV/mm |
| | ASTM D-257 | 1016 Ω.cm |
| dielectric constant | | ASTM D-150 | 3.5 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.60 |
| Mold Shrinkage | | ASTM D955 | 0.4-1.1 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648/ISO 75 | 220 ℃（℉） |
| Heat distortion temperature | | ASTM D648/ISO 75 | 205 ℃（℉） |
| Heat distortion temperature | | ASTM D-648 | 220 °C |
| Heat distortion temperature | | ASTM D-648 | 205 °C |
| combustibility | | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.