Epoxy 353ND Black Epoxy Technology Inc.

Typical Applications:

Electrical and electronic applications medical and nursing products adhesives seals impregnation applications bonding

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:

Certificates

No Data...

Technical Data Sheet

Cured Properties	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	ShoreD		85
LapShearStrength	23°C		>13.8	MPa
Relative permittivity	1kHz,23°C		3.09
Volume resistivity	23°C		>1.6E+13	ohms·cm
Dissipation factor	1kHz,23°C		5E-03
Uncured Properties	Test Condition	Test Method	Test Result	Test Unit
Color	--5		Amber
Color	Color	--6		Black
density	PartB		1.02	g/cm³
	density	PartA		1.22	g/cm³
		density	粘度7(23°C)		3.0to5.0	Pa·s
			density	固化时间(150°C)		1.0	hr
			density	density	Pot Life		180to240	min
optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity	1500nm		<3.0	%
thermosetting	Test Condition	Test Method	Test Result	Test Unit
Thermosetting components	PartA		按重量计算的混合比:10
	Thermosetting components	PartB		按重量计算的混合比:1.0
	Thermosetting components	Thermosetting components	Shelf Life(23°C)		52	wk
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Glass transition temperature			>90.0	°C
Linear coefficient of thermal expansion	MD：--3		5.4E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：--4		2.1E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Ionic type	Cl-		595	ppm
	Ionic type	K+		16	ppm
		Ionic type	Na+		52	ppm
		Ionic type	Ionic type	NH4+		1149	ppm
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
weight loss on heating	300°C		1.8	%
DegradationTemperature		TGA	420	°C
Shear Strength	23°C		35.2	MPa
operate temperature	Continuous		-55-225	°C
	operate temperature	Intermittent		-55-325	°C
	operate temperature	operate temperature	StorageModulus(23°C)		3.56	GPa
weight loss on heating	200°C		0.92	%
weight loss on heating	weight loss on heating	250°C		1.2	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.