'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC RX2530 451118 COVESTRO THAILAND
215
Form：Granules | Grade：Medical grade
Properties:
Flame retardantHigh mobility
Typical Applications:
Automotive ApplicationsLighting installationelectrical equipment
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Automotive Applications | Lighting installation | electrical equipment |
| Properties: | Flame retardant | High mobility |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -60°C | ISO 179/1eU | NoBreak | |
| -30°C | ISO 179/1eU | NoBreak | ||
| Charpy Notched Impact Strength | 23°C,Partial Break | ISO 7391 | 70 | kJ/m² |
| -30°C,Complete Break | ISO 7391 | 14 | kJ/m² | |
| Multi axis Instrumented Peak Impact Force | 23°C | ISO 6603-2 | 5300 | N |
| -30°C | ISO 6603-2 | 6200 | N | |
| Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 60.0 | J |
| -30°C | ISO 6603-2 | 70.0 | J | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | -30°C,Complete Break | ISO 7391 | 12 | kJ/m² |
| 23°C,Partial Break | ISO 7391 | 65 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| SelfIgnition | ASTM D1929 | 550 | °C | |
| FlashIgnitionTemperature | ASTM D1929 | 480 | °C | |
| Extreme Oxygen Index | ISO 4589-2 | 27 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Bending strain | 23°C | ISO 178 | 7.0 | % |
| bending strength | 23°C | ISO 178 | 100 | Mpa |
| 3.5%Strain,23°C | ISO 178 | 74.0 | Mpa | |
| Tensile modulus | 23°C | ISO 527-2/1 | 2400 | Mpa |
| tensile strength | Yield,23°C | ISO 527-2/50 | 67.0 | Mpa |
| Break,23°C | ISO 527-2/50 | 75.0 | Mpa | |
| Tensile strain | Yield,23°C | ISO 527-2/50 | 6.1 | % |
| Break,23°C | ISO 527-2/50 | 130 | % | |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | >50 | % |
| Bending modulus | 23°C | ISO 178 | 2400 | Mpa |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| thermal conductivity | 23°C | ISO 8302 | 0.20 | W/m/K |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 6.5E-05 | cm/cm/°C |
| MD：23to55°C | ISO 11359-2 | 6.5E-05 | cm/cm/°C | |
| Ball Pressure Test | 132°C | IEC 60695-10-2 | Pass | |
| Vicat softening temperature | -- | ISO 306/B120 | 142 | °C |
| -- | ISO 306/B50 | 141 | °C | |
| Glass transition temperature | ISO 11357-2 | 142 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 122 | °C |
| 0.45MPa,Unannealed | ISO 75-2/B | 134 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | MD:2.00mm3 | ISO 294-4 | 0.60 | % |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO 62 | 0.12 | % | |
| Apparent density | ISO 60 | 0.66 | g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 16 | g/10min |
| Melt Volume Flow Rate (MVR) | 300°C/1.2kg | ISO 1133 | 15.0 | cm3/10min |
| Shrinkage rate | TD | ISO 2577 | 0.60-0.80 | % |
| MD | ISO 2577 | 0.60-0.80 | % | |
| TD:2.00mm3 | ISO 294-4 | 0.65 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Volume resistivity | 23°C | IEC 60093 | 1E+16 | ohms·cm |
| Surface resistivity | IEC 60093 | 1E+16 | ohms | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Ball Pressure Test | ISO 2039-1 | 118 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.