Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ASTM D792 | 1.70to1.90 g/cm³ |
Shrinkage rate | | ASTM D1895 | 1.0to1.5 |
Shrinkage rate | | ASTM D955 | 0.050to0.30 % |
Water absorption rate | | ASTM D570 | 0.12 % |
hardness | Test Condition | Test Method | Test Result |
---|
Barcol Hardness | | ASTM D2583 | 41to47 |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | V-0 |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
tensile strength | | ASTM D638 | 34.5to44.8 MPa |
Flexural modulus | | ASTM D790 | 11700to13100 MPa |
bending strength | | ASTM D790 | 89.6to117 MPa |
Compression Modulus | | ASTM D695 | 345000to372000 MPa |
compressive strength | | ASTM D695 | 96.5to103 MPa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ASTM D256 | 370to530 J/m |
Electrical performance | Test Condition | Test Method | Test Result |
---|
dielectric strength | | ASTM D149 | >14 kV/mm |
arc resistance | | ASTM D495 | >185 sec |
Inclined plate electric trace | | ASTM D2303 | >1000 min |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ASTM D648 | >260 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.