| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTMD1238 | 1.0 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTMD2457 | 141 | |
| transparency | ASTMD1746 | 83.0 | |
| Haze ratio | ASTMD1003 | 1.1 % |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTMD882 | 58.6 Mpa | |
| ASTMD882 | 44.7 Mpa | ||
| elongation | ASTMD882 | 620 % | |
| ASTMD882 | 630 % | ||
| Falling hammer impact | ASTMD1709B | >830 g | |
| Elmondov tear strength 2 | ASTMD1922 | 550 g | |
| ASTMD1922 | 720 g | ||
| Initial sealing temperature 3 | 内部方法 | 85.0 °C | |
| Film thickness - tested | 51 µm | ||
| 内部方法 | 8.81 J | ||
| 内部方法 | 92.5 N | ||
| Membrane puncture resistance | 内部方法 | 22.3 J/cm³ | |
| Secant modulus | ASTMD882 | 91.7 Mpa | |
| ASTMD882 | 92.4 Mpa | ||
| tensile strength | ASTMD882 | 7.24 Mpa | |
| ASTMD882 | 6.89 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ASTMD1525 | 86.0 °C | |
| 内部方法 | 99.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.