ABS PA-727 BK TAIWAN CHIMEI

Form：Granules | Grade：Electroplating grade

Properties:

High glossHigh toughnessHigh rigidity

Typical Applications:

Automotive sectorHousehold goodsSanitary WareHome appliance shell

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive sector \| Household goods \| Sanitary Ware \| Home appliance shell
Properties:	High gloss \| High toughness \| High rigidity

Certificates

No Data...

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Break	ISO 527-2/50	25	%
Bending modulus	--5	ASTM D790	1720	Mpa
Bending modulus	Bending modulus	--6	ISO 178	2000	Mpa
bending strength	--5	ASTM D790	71.0	Mpa
bending strength	bending strength	--6	ISO 178	71.0	Mpa
tensile strength	Yield4	ASTM D638	45.4	Mpa
	tensile strength	Yield	ISO 527-2/50	46.0	Mpa
	tensile strength	tensile strength	Break	ISO 527-2/50	34.0	Mpa
elongation	Break4	ASTM D638	40	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	87.0	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	83.0	°C
		Hot deformation temperature	1.8MPa,Annealed	ASTM D648	97.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	100	°C
Vicat softening temperature	--	ASTM D15257	106	°C
	Vicat softening temperature	--	ISO 306/A50	105	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	98.0	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	8.8E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	200°C/5.0kg	ASTM D1238	1.6	g/10min
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	19.0	cm3/10min
Shrinkage rate		ISO 294-4	0.40-0.70	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	113

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.