PC HP1R-1H112 SABIC INNOVATIVE CANADA

Form：Granules

Properties:

High mobility

Typical Applications:

medical caremedicineMedical/nursing supplies

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	medical care \| medicine \| Medical/nursing supplies
Properties:	High mobility

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	65	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Dart impact	23°C,TotalEnergy	ASTM D3763	54.0	J
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	50.0mmSpan5	ASTM D790	2300	Mpa
Bending modulus	Bending modulus	--6	ISO 178	2300	Mpa
bending strength	--6,7	ISO 178	90.0	Mpa
bending strength	bending strength	Yield,50.0mmSpan5	ASTM D790	93.0	Mpa
Tensile modulus	--3	ASTM D638	2370	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2350	Mpa
tensile strength	Yield4	ASTM D638	62.0	Mpa
	tensile strength	Yield	ISO 527-2/50	63.0	Mpa
		tensile strength	Break4	ASTM D638	65.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	50.0	Mpa
elongation	Yield4	ASTM D638	6.0	%
	elongation	Yield	ISO 527-2/50	6.0	%
		elongation	Break4	ASTM D638	120	%
		elongation	elongation	Break	ISO 527-2/50	70	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	126	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,100mmSpan10	ISO 75-2/Ae	121	°C
Vicat softening temperature	--	ASTMD152511	139	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	140	°C
Linear coefficient of thermal expansion	MD:-40to95°C	ASTME831	6.8E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD:23to80°C	ISO 11359-2	7E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD:-40to95°C	ASTME831	6.8E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ISO 11359-2	7E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300°C/1.2kg	ASTM D1238	28	g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	26.0	cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70	%
Water absorption rate	Saturation,23°C	ISO 62	0.35	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.