Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | Resin | | 100 |
| Thermosetting components | Hardener | | 按重量计算的混合比:33 |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| density | | | 0.950to0.990 g/cm³ |
| Viscosity | | | 15to25 Pa·s |
| Curing Time | | | 4.0to5.0 hr |
| STORAGE STABILITY | | | 7.0to9.0 min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 7619 | 72to76 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO 178 | 1950to2450 MPa |
| bending strength | | ISO 178 | 20.0to24.0 MPa |
| compression stress | | ISO 604 | 26.0to32.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 1.8to2.2 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Martin's heat-resistant temperature | | DIN 53458 | 63to67 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.