Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| MediumDensity | | | 1.19 g/cm³ |
| SpecificHeatCapacity of Melt | | | 3000 J/kg/°C |
| melt mass-flow rate | | ISO1133 | 2.3 g/10min |
| Melt volume flow rate | | ISO1133 | 1.90 cm3/10min |
| Shrinkage rate | | ISO294-4 | 1.8 % |
| Shrinkage rate | | ISO294-4 | 2.2 % |
| Water absorption rate | | ISO62 | 0.90 % |
| Water absorption rate | | ISO62 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 90 |
| Rockwell hardness | | ISO2039-2 | 121 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| atomization | | ISO6452 | 91 % |
| atomization | | ISO6452 | 1E-04 g |
| Burning rate 3 | | ISO3795 | 30 mm/min |
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | IEC60695-11-10,-20 | HB |
| UL flame retardant rating | | IEC60695-11-10,-20 | HB |
| FMVSS flammability | | FMVSS302 | B |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Emission | | VDA275 | <8.00 mg/kg |
| Emissions of Organic Compounds | | VDA277 | 4.00 µgC/g |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 3000 Mpa |
| Tensile stress | | ISO527-2 | 72.0 Mpa |
| Tensile strain | | ISO527-2 | 26 % |
| Nominal tensile fracture strain | | ISO527-2 | 45 % |
| TensileCreepModule | | ISO899-1 | 2900 Mpa |
| Tensile creep modulus | | ISO899-1 | 1600 Mpa |
| Flexural modulus | | ISO178 | 2900 Mpa |
| Bending stress | | ISO178 | 79.0 Mpa |
| compression stress | | ISO604 | 110 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 430 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 3E+13 ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 41 KV/mm |
| | IEC60250 | 3.90 |
| | IEC60250 | 3.80 |
| Dissipation Factor | | IEC60250 | 1E-03 |
| Dissipation Factor | | IEC60250 | 5.5E-03 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO11359-2 | 1E-04 cm/cm/°C |
| | ISO11359-2 | 1.1E-04 cm/cm/°C |
| | ISO11359-2 | 1E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO11359-2 | 160 °C |
| Linear coefficient of thermal expansion | | ISO11359-2 | 30.0 min/mm |
| | ISO11359-2 | 1E-07 m²/s |
| | ISO75-2/B | 160 °C |
| | ISO75-2/A | 100 °C |
| vicat | | ISO306/A50 | 175 °C |
| vicat | | ISO306/B50 | 160 °C |
| melting temperature | | ISO11357-3 | 178 °C |
| | ISO11359-2 | 1.1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.