Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| ThermalConductivityofMelt | | | 0.24 W/m/K |
| density | | ISO1183 | 1.20 g/cm³ |
| Melt volume flow rate | | ISO1133 | 16.0 cm³/10min |
| Shrinkage rate | | ISO294-4 | 0.60 % |
| Water absorption rate | | ISO62 | 0.35 % |
| LimitingViscosity | | ISO1628-4 | 46.0 cm³/g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ISO2039-2 | 70 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTMD1003 | 89.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Hot filament ignition temperature | | IEC60695-2-13 | 875 °C |
| Limiting Oxygen Index | | ISO4589-2 | 26 % |
| UL flame retardant rating | | IEC60695-11-10,-20 | V-2 |
| UL flame retardant rating | | IEC60695-11-10,-20 | V-2 |
| Burning wire flammability index | | IEC60695-2-12 | 800 °C |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 825 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Yield | ISO527-2 | 6.0 % |
| Tensile modulus | | ISO527-2 | 2300 MPa |
| Tensile stress | Yield | ISO527-2 | 60.0 MPa |
| Nominal tensile fracture strain | | ISO527-2 | >50 % |
| Flexural modulus | | ISO178 | 2400 MPa |
| Bending stress | | ISO178 | 90.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/4A | 70 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | >1.0E+15 ohms |
| Dissipation Factor | | IEC60250 | 9.2E-03 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 2 |
| CTI | | IEC60112 | 225 V |
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 29 kV/mm |
| | IEC60250 | 3.00 |
| | IEC60250 | 2.90 |
| Dissipation Factor | | IEC60250 | 6.6E-04 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI Imp | | UL746 | 125 °C |
| RTI Imp | | UL746 | 130 °C |
| RTI Str | | UL746 | 125 °C |
| RTI Str | | UL746 | 130 °C |
| | ISO75-2/A | 130 °C |
| vicat | | ISO306/B50 | 145 °C |
| BallPressure Test | | IEC60695-10-2 | Pass |
| | ISO11359-2 | 6.5E-05 cm/cm/°C |
| RTI Elec | | UL746 | 130 °C |
| RTI Elec | | UL746 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.