Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.53 g/cm³ |
| melt mass-flow rate | | ISO1133 | 25 g/10min |
| Shrinkage rate | | STM640808 | 1.0 % |
| Shrinkage rate | | STM640808 | 0.93 % |
| water content | | ISO960 | 0.050 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Hot filament ignition temperature | | IEC60695-2-13 | 750 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178 | 3500 MPa |
| Bending stress | | ISO178 | 175 MPa |
| Tensile modulus | | ISO527-2 | 4150 MPa |
| Tensile stress | Yield | ISO527-2 | 60.0 MPa |
| Tensile strain | Yield | ISO527-2 | 6.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 4.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179 | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 45 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | 50 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+15 ohms |
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 25 kV/mm |
| CTI | | IEC60112 | 500 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | | ISO75-2/B | 195 °C |
| vicat | | ISO306/B | 215 °C |
| Melting temperature (DSC) | | ISO3146 | 225 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.