ABS SD-0150 BK Samsung Cheil South Korea

Form：Granules | Grade：Injection grade

Properties:

High impact resistance

Typical Applications:

Decorative componentsElectrical appliancesAutomotive sector

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Decorative components \| Electrical appliances \| Automotive sector
Properties:	High impact resistance

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Huangdu Index	3.20mm	ASTM D1925	18	YI
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180/1A	24	kJ/m²
	Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	240	J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	280	J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	28	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	59.0	Mpa
bending strength	bending strength		ASTM D790	58.0	Mpa
Bending modulus		ISO 178	2100	Mpa
Bending modulus	Bending modulus		ASTM D790	2100	Mpa
Tensile strain	Break	ISO 527-2/50	14	%
elongation	Break	ASTM D638	15	%
tensile strength	Break	ISO 527-2/50	35.0	Mpa
	tensile strength	Break	ASTM D638	44.0	Mpa
		tensile strength	Yield	ISO 527-2/50	41.0	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	40.0	Mpa
Tensile modulus		ISO 527-2/50	2400	Mpa
Tensile modulus	Tensile modulus		ASTM D638	2000	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ISO 306/B50	98.0	°C
Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	78.0	°C
	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	83.0	°C
		Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	91.0	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	95.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD:3.20mm	ISO 2577	0.30	%
density		ASTM D792	1.04	g/cm³
density	density		ISO 1183	1.04	g/cm³
melt mass-flow rate	200°C/5.0kg	ASTM D1238	1.7	g/10min
melt mass-flow rate	melt mass-flow rate	200°C/5.0kg	ISO 1133	1.7	g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.30	%
	Shrinkage rate	TD：3.20mm	ASTM D955	0.30	%
	Shrinkage rate	Shrinkage rate	TD:3.20mm	ISO 2577	0.30	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ISO 2039-2	108
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	108

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.