CONDITION	Test Condition	Test Method	Test Result	Test Unit
Pre drying temperature		-	70~80	℃
Pre drying time		-	3~4	hrs
Temperature		-	200~250	℃
Mold temperature		-	40~80	℃
Screw speed		-	30~60	rpm
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield，23℃, 50mm/min, 3.2mm	ASTM D638	42	Mpa
Elongation at Break	23℃, 50mm/min, 3.2mm	ASTM D638	≥10	%
bending strength	23℃, 10mm/min, 6.4mm	ASTM D790	70	Mpa
Bending modulus	23℃, 10mm/min, 6.4mm	ASTM D790	2350	Mpa
Izod Notched Impact Strength	Notched, 3.2mm, 23℃	ASTM D256	270	J/m
Izod Notched Impact Strength	Izod Notched Impact Strength	Notched, 6.4mm, 23℃	ASTM D256	250	J/m
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	Edgewise,1.82MPa,6.4mm,Unannealed	ASTM D648	85	℃
Vicat softening temperature	50N, 50℃/h	ASTM D1525	93	℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density	23℃	ASTM D792	1.04	g/cm³
Shrinkage rate	23℃, 3.2mm	ASTM D955	0.4~0.7	%
melt mass-flow rate	220℃, 10kg	ASTM D1238	40	g/10min
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness		ASTM D785	106	R

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.