| 物理性能 | Test Condition | Test Method | Test Result |
|---|
| 密度 | | ASTMD792 | 1.10 g/cm³ |
| 吸水率 | 饱和,6.99mm | ASTMD570 | 0.19 % |
| 补充信息 | Test Condition | Test Method | Test Result |
|---|
| CyclesFreeze-Thaw- | -29到82°C,6.99mm | 内部方法 | NoEffect |
| HotFormingTemperature | ABSSide:6.99mm | 内部方法 | 149到171 °C |
| HotFormingTemperature | AcrylicSide:6.99mm | 内部方法 | 177到193 °C |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|
| 拉伸模量 | 6.99mm | ASTMD638 | 2620 MPa |
| 抗张强度 | 屈服,6.99mm | ASTMD638 | 44.8 MPa |
| 伸长率 | 断裂,6.99mm | ASTMD638 | 5.0 % |
| 弯曲模量 | 6.99mm4 | ASTMD790 | 2140 MPa |
| 弯曲模量 | 6.99mm5 | ASTMD790 | 2160 MPa |
| 弯曲强度 | 6.99mm4 | ASTMD790 | 68.9 MPa |
| 弯曲强度 | 6.99mm5 | ASTMD790 | 74.5 MPa |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|
| UL阻燃等级 | 7.0mm | UL94 | HB |
| 硬度 | Test Condition | Test Method | Test Result |
|---|
| 洛氏硬度 | M级,6.99mm | ASTMD785 | 97 |
| 巴氏硬度 | 6.99mm | ASTMD2583 | 52 |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|
| 热变形温度 | 1.8MPa,未退火,6.99mm | ASTMD648 | 89.4 °C |
| 线性热膨胀系数 | MD：6.99mm | ASTMD696 | 7.9E-05 cm/cm/°C |
| 悬壁梁缺口冲击强度 | 6.99mm | ASTMD256A | 130 J/m |
| 装有测量仪表的落镖冲击 | 6.99mm | 内部方法 | >40.7 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.