Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD1505 | 1.29 g/cm³ |
| Water absorption rate | | ASTMD570 | <0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 80 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | | 1.639 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Hydrogen | | ASTMD1434 | 43 cm³·mm/m²/atm/24hr |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| | ASTMD1894 | 0.29 |
| | ASTMD1894 | 0.29 |
| film | Test Condition | Test Method | Test Result |
|---|
| Secant modulus MD | | ASTMD882 | 2760 MPa |
| tensile strength | Yield | ASTMD882 | 55.2 MPa |
| tensile strength | Break | ASTMD882 | 68.9 MPa |
| elongation | Yield | ASTMD882 | 2.9 % |
| elongation | Break | ASTMD882 | <200 % |
| oxygen permeability | | ASTMD1434 | 2.8 cm³·mm/m²/atm/24hr |
| Water vapor permeability | | ASTMF1249 | 0.080 g·mm/m²/atm/24hr |
| CarbonDioxidePermeability | | ASTMD1434 | 3.0 cm³·mm/m²/atm/24hr |
| NitrogenPermeability | | ASTMD1434 | 0.40 cm³·mm/m²/atm/24hr |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTMD150 | 3.10 |
| dielectric constant | | ASTMD150 | 2.95 |
| Dissipation Factor | | ASTMD150 | 0.020 |
| Dissipation Factor | | ASTMD150 | 0.019 |
| Dissipation Factor | | ASTMD150 | 0.013 |
| Surface Resistivity | | ASTMD257 | 1E+14 ohms |
| Volume resistivity | | ASTMD257 | 8.8E+16 ohms·cm |
| dielectric strength | | ASTMD149 | 220 kV/mm |
| dielectric constant | | ASTMD150 | 3.15 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | | 80.0 °C |
| melting temperature | | DSC | 290 °C |
| | TMA | 3.5E-05 cm/cm/°C |
| specific heat | | | 712 J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.084 W/m/K |
| Service | | | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.