EAA 3460 DOW USA
PRIMACOR™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | DOW USA/3460 |
|---|---|---|---|
| Starting temperature of heat sealing | Internal Method | 85 ℃ | |
| Water Vapor Transmission Rate | 38℃，90% RH | DIN 53122/2 | g·mm/m |
| film | Test Condition | Test Method | DOW USA/3460 |
|---|---|---|---|
| Water Vapor Transmission Rate | 38°C,90%RH | DIN 53122/2 | 0.44 g·mm/m²/atm/24hr |
| Initial sealing temperature | 内部方法 | 85.0 °C |
| Basic performance | Test Condition | Test Method | DOW USA/3460 |
|---|---|---|---|
| Monomer content | Internal Method | % |
| Mechanical properties | Test Condition | Test Method | DOW USA/3460 |
|---|---|---|---|
| tensile strength | 屈服,模压成型 | ASTMD638 | 7.24 Mpa |
| elongation at break | Compression Molded | ASTM D-638 | 580 % |
| Compression Molded | ISO 527-2 | 580 MPa | |
| elongation | 断裂,模压成型 | ASTMD638 | 580 % |
| tensile strength | 屈服,Compression Molded | ISO 527-2 | 7.24 MPa |
| Compression Molded，断裂 | ASTM D-638 | 16.2 MPa | |
| 屈服,Compression Molded | ASTM D-638 | 7.24 MPa | |
| Compression Molded，断裂 | ISO 527-2 | 16.2 MPa | |
| 断裂,模压成型 | ASTMD638 | 16.2 Mpa |
| physical property | Test Condition | Test Method | DOW USA/3460 |
|---|---|---|---|
| Content of comonomer | 内部方法 | 9.7 % | |
| melt mass-flow rate | 190°C/2.16kg | ASTMD1238 | 20 g/10min |
| Thermal performance | Test Condition | Test Method | DOW USA/3460 |
|---|---|---|---|
| melting temperature | 内部方法 | 95.0 °C | |
| vicat | ASTM D-1525 | 72.2 ℃ | |
| ISO 306 | 72.2 ℃ | ||
| melting temperature | Internal Method | ℃ | |
| vicat | ASTMD1525 | 72.2 °C |