PBT HR5315HFS NC010 DUPONT USA
Cristin®
Automotive components,Electronic and Electrical Applications
High mobility,Easy to form,Easy to process
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/HR5315HFS NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 60 kJ/m² |
| -30°C | ISO 179/1eU | 30 kJ/m² |
| thermal performance | Test Condition | Test Method | DUPONT USA/HR5315HFS NC010 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 200 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C | |
| Glass Transition Temperature | ISO 11357-2 | 65.0 °C | |
| melting temperature | ISO 11357-3 | 225 °C |
| mechanical properties | Test Condition | Test Method | DUPONT USA/HR5315HFS NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 5000 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 100 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 3.4 % |
| bending strength | ISO 178 | 145 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT USA/HR5315HFS NC010 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 42 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.60 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.010 |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 3.50 |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.010 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Physical properties | Test Condition | Test Method | DUPONT USA/HR5315HFS NC010 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.15 % |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 12.0 cm3/10min |
| FlowLength2 | 2.00mm，FlowLength | 400 mm | |
| melt viscosity | 250°C,1000sec^-1 | ISO 11443 | 175000 mPa·s |
| shrinkage rate | TD | ISO 294-4 | 1.1 % |
| Ejection Temperature | 170 °C | ||
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.40 % |
| shrinkage rate | MD | ISO 294-4 | 0.50 % |
| flammability | Test Condition | Test Method | DUPONT USA/HR5315HFS NC010 |
|---|---|---|---|
| FMVSS flammability | FMVSS302 | B | |
| Flammability level | 1.5mm | IEC 60695-11-10,-20 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 20 % | |
| burning rate | 1.00mm | ISO 3795 | 32 mm/min |