ABS/PC 8002-100 SABIC INNOVATIVE NANSHA
CYCOLOY™
Home appliance components、Automotive sector、Electronic field、Electrical field、Application in the automo
heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/8002-100 |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 61.0 J |
| -30°C,TotalEnergy | ASTM D3763 | 54.2 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/8002-100 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2210 Mpa | |
| elongation | 断裂 | ASTM D638 | 150 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 86.2 Mpa |
| elongation | 屈服 | ASTM D638 | 5.0 % |
| tensile strength | 屈服 | ASTM D638 | 56.5 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2340 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/8002-100 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 24hr | ASTM D570 | 0.10 % |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 9.0 g/10min |
| Water absorption rate | 平衡,23°C | ASTM D570 | 0.40 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/8002-100 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 110 °C |
| thermal conductivity | ASTMC177 | 0.20 W/m/K | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 124 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 107 °C |