Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PC EXL1433T SABIC INNOVATIVE NANSHA

LEXAN™

Automotive sector,Electronic and Electrical Applications,Plastic bag

Middle flow,High ductility at low tem,Short molding cycle

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1433T
Rockwell hardness	L-Sale	ISO 2039-2	90
Rockwell hardness		L-Sale	ASTM D785	90

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1433T
1.8MPa, unannealed, 3.20mm		ASTM D648	124 °C
1.8MPa, unannealed, 64.0mm span of		ISO 75-2/Af	119 °C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Flow: 23 to 80 ° C	23to80℃	ISO 11359-2	7.2E-05 cm/cm/°C
Flow: -40 to 95 ° C	-40to95℃	ASTME831	7.2E-05 cm/cm/°C
Horizontal: 23 to 80 ° C	Across Flow, 23to80℃	ISO 11359-2	7.9E-05 cm/cm/°C
Horizontal: -40 to 95 ° C	Across Flow, -40to95℃	ASTME831	7.9E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	124 °C
Hot deformation temperature		1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	119 °C
Linear coefficient of thermal expansion	TD：23to80°C	ISO 11359-2	7.9E-05 cm/cm/°C
		MD：-40to95°C	ASTME831	7.2E-05 cm/cm/°C
		MD：23to80°C	ISO 11359-2	7.2E-05 cm/cm/°C
		TD：-40to95°C	ASTME831	7.9E-05 cm/cm/°C
RTI		UL 746	130 °C
RTI Elec		UL 746	130 °C
RTI Str		UL 746	130 °C
Vicat softening temperature	--	ISO 306/B120	142 °C
		--	ISO 306/B50	141 °C
			ASTM D152510	141 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1433T
--1		ASTM D638	2220 Mpa
50.0mm span		ASTM D790	2220 Mpa
--7		ISO 178	2150 Mpa
--8		ISO 178	90.2 Mpa
Bending modulus	50.0mmSpan	ASTM D790	2220 Mpa
Bending modulus			ISO 178	2150 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	94.3 Mpa
bending strength			ISO 178	90.2 Mpa
crack		ASTM D638	64.1 Mpa
			ASTM D638	130 %
			ISO 527-2/50	61.5 Mpa
			ISO 527-2/50	120 %
elongation	Break	ASTM D638	130 %
elongation		Yield	ASTM D638	5.8 %
Tensile modulus		ASTM D638	2220 Mpa
Tensile modulus			ISO 527-2/1	2350 Mpa
Tensile strain	Break	ISO 527-2/50	120 %
Tensile strain		Yield	ISO 527-2/50	5.5 %
tensile strength	Break	ASTM D638	64.1 Mpa
		Yield	ASTM D638	58.0 Mpa
		Yield	ISO 527-2/50	57.9 Mpa
		Break	ISO 527-2/50	61.5 Mpa
yield		ASTM D638	5.8 %
			ASTM D638	58.0 Mpa
			ISO 527-2/50	5.5 %
			ISO 527-2/50	57.9 Mpa
Yield, 50.0mm span		ASTM D790	94.3 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1433T
Surface resistivity		ASTM D257	>1.0E+15 ohms
Volume resistivity		ASTM D257	>1.0E+15 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1433T
melt mass-flow rate	300°C/1.2kg	ASTM D1238	10 g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	9.50 cm3/10min
Shrinkage rate	TD:3.20mm	Internal Method	0.40-0.80 %
		TD：3.20mm	Internal Method	0.40-0.80 %
		MD：3.20mm	Internal Method	0.40-0.80 %
		MD:3.20mm	Internal Method	0.40-0.80 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.093 %
Water absorption rate		Saturation,23°C	ISO 62	0.12 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1433T
23°C		ASTM D256	890 J/m
23°C			ISO 180/1A	65 kJ/m²
-30°C		ASTM D256	800 J/m
-30°C			ISO 180/1A	45 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	70 kJ/m²
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	50 kJ/m²
Dart impact	-30°C,TotalEnergy	ASTM D3763	85.0 J
Dart impact		23°C,TotalEnergy	ASTM D3763	82.4 J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	65 kJ/m²
Impact strength of cantilever beam gap		-30°C	ISO 180/1A	45 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength		23°C	ISO 180/1U	无断裂

flammability	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1433T
Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
Burning wire flammability index		3.00mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	0.800mm	IEC 60695-2-13	825 °C
		3.00mm	IEC 60695-2-13	825 °C
		3.0mm	IEC 60695-2-13	825 °C
		0.8mm	IEC 60695-2-13	825 °C
UL flame retardant rating	2.5mm	UL 94	V-2
		3.0mm	UL 94	V-2
		2.50mm	UL 94	V-2

optical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1433T
transmissivity	2540μm	ASTM D1003	82.0 %
turbidity	2540μm	ASTM D1003	3.0 %