MMBS DENKA Transparent Polymer TH-23 DENKA JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DENKA JAPAN/DENKA Transparent Polymer TH-23 |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 12 kJ/m² |
| hardness | Test Condition | Test Method | DENKA JAPAN/DENKA Transparent Polymer TH-23 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 29 |
| Mechanical properties | Test Condition | Test Method | DENKA JAPAN/DENKA Transparent Polymer TH-23 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2/5 | 34 % | |
| tensile strength | 屈服 | ISO 527-2/5 | 44.0 MPa |
| Flexural modulus | ISO 178 | 2100 MPa | |
| bending strength | ISO 178 | 65.0 MPa |
| optical performance | Test Condition | Test Method | DENKA JAPAN/DENKA Transparent Polymer TH-23 |
|---|---|---|---|
| transmissivity | 2000µm | ISO 13468-1 | 91.0 % |
| Haze ratio | 2000µm | ISO 14782 | 2.7 % |
| flammability | Test Condition | Test Method | DENKA JAPAN/DENKA Transparent Polymer TH-23 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | DENKA JAPAN/DENKA Transparent Polymer TH-23 |
|---|---|---|---|
| Shrinkage rate | 2.00mm | 内部方法 | 0.40 % |
| density | 23°C | ISO 1183 | 1.08 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ISO 1133 | 3.9 g/10min |
| 220°C/10.0kg | ISO 1133 | 59 g/10min |
| Thermal performance | Test Condition | Test Method | DENKA JAPAN/DENKA Transparent Polymer TH-23 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 63.0 °C |
| vicat | ISO 306/B | 84.0 °C |