Product Name

Brand Name

Usages

Properties

Certificates

LCP A330S VF2001 JAPAN POLYPLASTIC

LAPEROS®

Automotive sector,Camera applications,Optical applications,Electronic field,Electrical field,Automotive Applications,Enterprise Equipment,Camera applications,Electrical/Electronic Applications,Optical applications

Antichemical,Thermal stability,high strength,wear resistant,Weather resistance,High rigidity,damping,Electrical insulation mat,Good chemical corrosion r,Good thermal stability,Good thermal stability,High traffic,Solvent resistant,Good wear resistance,high strength,Good weather resistance

Plastic Datasheets

thermal performance	Test Condition	Test Method	JAPAN POLYPLASTIC/A330S VF2001
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	210 ℃
Linear coefficient of thermal expansion	50℃,3.00mm，Flow	ASTM D696	5E-06 cm/cm/℃
Linear coefficient of thermal expansion		50℃,3.00mm，垂直	ASTM D696	0.000062 cm/cm/℃
UL flame retardant rating	1.60mm	UL 94	V-0
		0.400mm	UL 94	V-0
		0.800mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	JAPAN POLYPLASTIC/A330S VF2001
Bending modulus	6.4mm	ASTM D790	14700 MPa
bending strength	6.4mm	ASTM D790	215 MPa
Elongation at Break	3.20mm	ASTM D638	2.5 %
Impact strength of cantilever beam gap		ASTM D256	58 J/m
tensile strength	3.20mm	ASTM D638	205 MPa

Electrical performance	Test Condition	Test Method	JAPAN POLYPLASTIC/A330S VF2001
Arc resistance		ASTM D495	124 sec
Compared to the anti leakage trace index		UL 746	V
Dielectric constant	1000Hz	ASTM D150	4.6
Dielectric constant		1E+6Hz	ASTM D150	0.027
Dielectric strength	3.00mm	ASTM D149	24 kV/mm
Surface resistivity		ASTM D257	8.1E+15 ohms
Volume resistivity		ASTM D257	2E+16 Ohm.cm

Physical properties	Test Condition	Test Method	JAPAN POLYPLASTIC/A330S VF2001
Rockwell hardness	M-Scale	ASTM D785	72
Shrinkage rate	Flow	ASTM D955	0.02 %
Shrinkage rate		Across Flow	ASTM D955	-0.05 %