Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS AG15E1-H FCFC TAIWAN
TAIRILAC®
Toy、suitcase、Phone、calculator、Clock housing、Sound enclosure
High gloss、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | FCFC TAIWAN/AG15E1-H |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ASTM D785 | 110 |
| R计秤,23°C | ISO 2039-2 | 110 |
| Mechanical properties | Test Condition | Test Method | FCFC TAIWAN/AG15E1-H |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 86.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 52.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2750 Mpa |
| bending strength | 23°C | ASTM D790 | 85.3 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 2750 Mpa |
| tensile strength | 23°C | ASTM D638 | 52.0 Mpa |
| flammability | Test Condition | Test Method | FCFC TAIWAN/AG15E1-H |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | FCFC TAIWAN/AG15E1-H |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.40-0.70 % |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 1.8 g/10min |
| 200°C/5.0kg | ISO 1133 | 1.8 g/10min | |
| 220°C/10.0kg | ASTM D1238 | 20 g/10min | |
| 220°C/10.0kg | ISO 1133 | 20 g/10min |
| Thermal performance | Test Condition | Test Method | FCFC TAIWAN/AG15E1-H |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,12.7mm，HDT | ISO 75-2/A | 84.0 °C |
| vicat | ASTM D15253 | 103 °C | |
| Heat distortion temperature | 1.8MPa,未退火,12.7mm，HDT | ASTM D648 | 84.0 °C |
| 1.8MPa,退火，HDT | ISO 75-2/A | 94.0 °C | |
| vicat | ISO 306/A | 103 °C | |
| Heat distortion temperature | 1.8MPa,Annealed，HDT | ASTM D648 | 94.0 °C |