Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS/PC LG9000-701USDD SABIC INNOVATIVE US
CYCOLAC™
Automotive sector
UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000-701USDD |
|---|---|---|---|
| Dart impact | -30°C, Total Energy | ASTM D3763 | 33.0 J |
| 23°C, Total Energy | ASTM D3763 | 40.0 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000-701USDD |
|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000-701USDD |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 75 % |
| bending strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 84.0 Mpa |
| tensile strength | 屈服 | ASTM D638 | 54.0 Mpa |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 2300 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000-701USDD |
|---|---|---|---|
| Hot wire ignition (HWI) | UL 746 | PLC 2 | |
| arc resistance | ASTM D495 | PLC 6 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000-701USDD |
|---|---|---|---|
| gloss | 60°, 无织构 | ASTM D523 | 30 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000-701USDD |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000-701USDD |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C | ASTM D570 | 0.40 % |
| Shrinkage rate | 横向流动 : 3.20 mm | 内部方法 | 0.50 - 0.70 % |
| Water absorption rate | 24 hr | ASTM D570 | 0.10 % |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.50 - 0.70 % |
| melt mass-flow rate | 260°C/5.0 kg | ASTM D1238 | 17 g/10 min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000-701USDD |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -20 到 150°C | ASTM E831 | 7.2E-5 cm/cm/°C |
| vicat | ASTM D15254 | 129 °C | |
| thermal conductivity | ASTM C177 | 0.20 W/m/K | |
| Linear coefficient of thermal expansion | 横向 : -20 到 150°C | ASTM E831 | 7.2E-5 cm/cm/°C |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 123 °C |
| 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 110 °C | |
| RTI Imp | UL 746 | 60.0 °C | |
| RTI | UL 746 | 60.0 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 129 °C |
| 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 107 °C | |
| RTI Elec | UL 746 | 60.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/LG9000-701USDD |
|---|---|---|---|
| screw speed | 40 to 70 rpm | ||
| Suggested maximum moisture content | 0.040 % | ||
| Processing (melt) temperature | 275 to 300 °C | ||
| drying temperature | 105 to 110 °C | ||
| Suggested injection volume | 30 to 80 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 255 to 295 °C | ||
| Temperature at the rear of the barrel | 250 to 290 °C | ||
| Exhaust hole depth | 0.038 to 0.076 mm | ||
| Temperature at the front of the material cylinder | 260 to 300 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 60 to 90 °C | ||
| Spray nozzle temperature | 275 to 300 °C |