ABS ABS A100HIE-84 Chase Plastics Services Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Chase Plastics Services Inc./ABS A100HIE-84 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 430 J/m |
| Dart impact | ASTM D3763 | 33.3 J |
| Mechanical properties | Test Condition | Test Method | Chase Plastics Services Inc./ABS A100HIE-84 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 32 % |
| 屈服 | ASTM D638 | 3.1 % | |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 63.4 MPa |
| Tensile modulus | ASTM D638 | 2030 MPa | |
| tensile strength | 断裂 | ASTM D638 | 29.0 MPa |
| 屈服 | ASTM D638 | 39.3 MPa | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2100 MPa |
| physical property | Test Condition | Test Method | Chase Plastics Services Inc./ABS A100HIE-84 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.60to0.80 % |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 4.00 cm³/10min |
| density | ASTM D792 | 1.03 g/cm³ |
| Thermal performance | Test Condition | Test Method | Chase Plastics Services Inc./ABS A100HIE-84 |
|---|---|---|---|
| vicat | ASTM D1525 | 107 °C | |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 1E-04 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 93.3 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 1E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 80.6 °C |