PA6 A1022GFL UNITIKA JAPAN
UNITIKA
Engine hood parts、Construction application 、Automotive sector、container、Electrical enclosure、Application in the automo、Parts under the hood of a、Architectural application、Vehicle electronics
Glass fiber reinforced、enhance、Filler: Glass fiber reinf、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | UNITIKA JAPAN/A1022GFL |
|---|---|---|---|
| Impact strength of simply supported beam without notch | kJ/m² | 23 33 |
| hardness | Test Condition | Test Method | UNITIKA JAPAN/A1022GFL |
|---|---|---|---|
| Rockwell hardness | R计秤 | 116 103 |
| Mechanical properties | Test Condition | Test Method | UNITIKA JAPAN/A1022GFL |
|---|---|---|---|
| Flexural modulus | MPa | 5000 2800 | |
| Bending stress | MPa | 175 | |
| Tensile strain | 断裂 | % | 2.7 4.6 |
| Tensile modulus | MPa | 5600 3000 | |
| Tensile stress | 断裂 | MPa | 120 70.0 |
| Electrical performance | Test Condition | Test Method | UNITIKA JAPAN/A1022GFL |
|---|---|---|---|
| dielectric constant | 1MHz | 3.30 -- | |
| Volume resistivity | ohms·cm | 2E+15 8E+13 | |
| dielectric strength | 1.00mm | kV/mm | 39 |
| flammability | Test Condition | Test Method | UNITIKA JAPAN/A1022GFL |
|---|---|---|---|
| UL flame retardant rating | 0.9mm | HB HB |
| physical property | Test Condition | Test Method | UNITIKA JAPAN/A1022GFL |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | % | 0.80到1.0 0.80到1.0 |
| MD:3.20mm | % | 0.30到0.50 0.30到0.50 | |
| Water absorption rate | 23°C,24hr | % | 1.5 1.5 |
| 平衡,23°C,50%RH | % | 2.4 2.4 |
| Thermal performance | Test Condition | Test Method | UNITIKA JAPAN/A1022GFL |
|---|---|---|---|
| 1.8MPa,未退火 | °C | 190 -- | |
| 0.45MPa,未退火 | °C | 214 -- | |
| MD | cm/cm/°C | 4.2E-05 4.2E-05 |