PBT 1151W-X01-BK TORAY JAPAN
Toraycon®
Automotive sector
Low warpage,Filler: glass beads, fibe,40% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | TORAY JAPAN/1151W-X01-BK |
---|---|---|---|
Impact strength of simply supported beam without notch | 23°C | ISO 179 | 55 kJ/m² |
Supplementary Information | Test Condition | Test Method | TORAY JAPAN/1151W-X01-BK |
---|---|---|---|
BarFlowLength | 250°C,1.00mm | 内部方法 | 8.50 CM |
hardness | Test Condition | Test Method | TORAY JAPAN/1151W-X01-BK |
---|---|---|---|
Rockwell hardness | M计秤,23°C | ISO 2039-2 | 65 |
Electrical performance | Test Condition | Test Method | TORAY JAPAN/1151W-X01-BK |
---|---|---|---|
dielectric constant | 23°C,50Hz | IEC 60250 | 3.50 |
23°C,1kHz | IEC 60250 | 3.50 | |
dielectric strength | IEC 60243-1 | 19 KV/mm | |
Volume resistivity | IEC 60093 | 4E+16 ohms·cm | |
arc resistance | IEC 60950 | 120 sec | |
Dissipation Factor | 23°C,50Hz | IEC 60250 | 2E-03 |
23°C,1MHz | IEC 60250 | 0.020 |
Mechanical properties | Test Condition | Test Method | TORAY JAPAN/1151W-X01-BK |
---|---|---|---|
Friction coefficient - vs. Metal | SuzukiMethod | 0.15 | |
Tensile strain | 断裂,23°C | ISO 527-2 | 3.0 % |
bending strength | 23°C | ISO 178 | 183 Mpa |
tensile strength | 屈服,23°C | ISO 527-2 | 110 Mpa |
Flexural modulus | 23°C | ISO 178 | 10000 Mpa |
coefficient of friction | 0.19 | ||
Tensile modulus | 23°C | ISO 527-2 | 10500 Mpa |
flammability | Test Condition | Test Method | TORAY JAPAN/1151W-X01-BK |
---|---|---|---|
UL flame retardant rating | UL 94 | HB |
physical property | Test Condition | Test Method | TORAY JAPAN/1151W-X01-BK |
---|---|---|---|
Shrinkage rate | TD:3.00mm2 | 内部方法 | 0.70 % |
MD:3.00mm4 | 内部方法 | 0.30 % | |
Water absorption rate | 23°C,24hr | ISO 62 | 0.080 % |
Thermal performance | Test Condition | Test Method | TORAY JAPAN/1151W-X01-BK |
---|---|---|---|
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 220 °C |
1.8MPa,未退火,HDT | ISO 75-2/A | 205 °C | |
Linear coefficient of thermal expansion | MD:-30到100°C | ISO 11359-2 | 3.8E-05 cm/cm/°C |