Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO GFN1720-780 SABIC INNOVATIVE US
NORYL™
Automotive components、Laptop case
High temperature resistan、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/GFN1720-780 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 25 kJ/m² |
| 23°C | ISO 180/1U | 28 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 21.7 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 9.4 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 35 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 11 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 33 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/GFN1720-780 |
|---|---|---|---|
| Rockwell hardness | L计秤 | ASTM D785 | 104 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/GFN1720-780 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 4400 Mpa | |
| bending strength | 屈服,50.0mm跨距4 | ASTM D790 | 116 Mpa |
| Tensile modulus | ASTM D638 | 4350 Mpa | |
| elongation | 断裂 | ASTM D638 | 3.0 % |
| bending strength | ISO 178 | 122 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| Flexural modulus | ISO 178 | 4160 Mpa | |
| 100mmSpan5 | ASTM D790 | 3590 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 63.0 Mpa |
| 断裂 | ISO 527-2 | 64.0 Mpa | |
| Flexural modulus | 50.0mm跨距4 | ASTM D790 | 3840 Mpa |
| bending strength | Yield,100mmSpan5 | ASTM D790 | 108 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/GFN1720-780 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 4 |
| Dissipation Factor | 1MHz | ASTM D150 | 1.4E-03 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 5 |
| dielectric constant | 1MHz | ASTM D150 | 2.90 |
| arc resistance | ASTM D495 | PLC7 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/GFN1720-780 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/GFN1720-780 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20-0.50 % |
| Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 16.4 cm3/10min |
| Water absorption rate | 24hr | ASTM D570 | 0.060 % |
| melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 17 g/10min |
| Outdoor applicability | UL 746C | f1 |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/GFN1720-780 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Be | 132 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 125 °C | |
| vicat | -- | ISO 306/B120 | 134 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.1E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 131 °C |
| vicat | -- | ISO 306/B50 | 131 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 5.1E-05 cm/cm/°C |
| RTI Imp | UL 746 | 90.0 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Ae | 124 °C |
| RTI Str | UL 746 | 90.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 122 °C |
| RTI Elec | UL 746 | 90.0 °C |