PC DX15354 BKNAT SABIC INNOVATIVE NANSHA
LNP™ THERMOCOMP™
Electronic appliances
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX15354 BKNAT |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 2200 J/m |
| 23°C4 | ISO 180/1U | 180 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX15354 BKNAT |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 2920 Mpa |
| elongation | 断裂3 | ASTM D638 | 11 % |
| bending strength | -- | ASTM D790 | 111 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 11 % |
| Flexural modulus | -- | ISO 178 | 2880 Mpa |
| bending strength | -- | ISO 178 | 112 Mpa |
| tensile strength | 断裂3 | ASTM D638 | 59.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2940 Mpa |
| Flexural modulus | -- | ASTM D790 | 2890 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 58.0 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX15354 BKNAT |
|---|---|---|---|
| dielectric constant | 1.10GHz | 内部方法 | 2.95 |
| Dissipation Factor | 1.10GHz | 内部方法 | 6E-03 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX15354 BKNAT |
|---|---|---|---|
| Melt volume flow rate | 330°C/2.16kg | ISO 1133 | 63.0 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.13 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX15354 BKNAT |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 6.7E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 168 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 155 °C | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 6.3E-05 cm/cm/°C |