Polyolefin, Unspecified Macromeric® 0103-212 BK USA Saco Polymers
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | USA Saco Polymers/Macromeric® 0103-212 BK |
|---|---|---|---|
| Shore hardness | 邵氏D,1秒 | ASTM D2240 | 55 |
| 邵氏A,1秒 | ASTM D2240 | 92 |
| Mechanical properties | Test Condition | Test Method | USA Saco Polymers/Macromeric® 0103-212 BK |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 200 % |
| tensile strength | 断裂 | ASTM D638 | 11.4 MPa |
| Flexural modulus | ASTM D790 | 262 MPa |
| flammability | Test Condition | Test Method | USA Saco Polymers/Macromeric® 0103-212 BK |
|---|---|---|---|
| Limiting Oxygen Index | ASTM D2863 | 37 % |
| aging | Test Condition | Test Method | USA Saco Polymers/Macromeric® 0103-212 BK |
|---|---|---|---|
| Change rate of tensile strength in air | 70°C,4hr,inOil | ASTM D471 | -25 % |
| ASTM D638 | 110 % | ||
| Change rate of ultimate elongation in air | 121°C,336hr | ASTM D573 | -40 % |
| 136°C,168hr | ASTM D573 | -40 % | |
| Tensile StrainatBreak Retention | ASTM D638 | 85 % | |
| Change rate of tensile strength in air | 136°C,168hr | ASTM D573 | 25 % |
| Change rate of ultimate elongation in air | 70°C,4hr,在油中 | ASTM D471 | 0.0 % |
| Change rate of tensile strength in air | 121°C,336hr | ASTM D573 | 30 % |
| physical property | Test Condition | Test Method | USA Saco Polymers/Macromeric® 0103-212 BK |
|---|---|---|---|
| melt mass-flow rate | 190°C/21.6kg | ASTM D1238 | 1.0 g/10min |
| Ash content ProcedureB | ASTM D5630 | 44 % | |
| density | ASTM D792 | 1.52 g/cm³ |
| Thermal performance | Test Condition | Test Method | USA Saco Polymers/Macromeric® 0103-212 BK |
|---|---|---|---|
| brittle temperature | ASTM D746 | -30.0 °C |