ABS PA-717C TAIWAN CHIMEI
POLYLAC® 
Washing machine,Home appliance components
High impact resistance
ULRoHSMSDSTDSTDSULMSDSRoHSSVHCProcessingStatement
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

machinabilityTest ConditionTest MethodTAIWAN CHIMEI/PA-717C
Dry conditions于80°C下烘料约2-3小时
Melt Temperature- °C
Mold temperature30-70°C °C
pressure- Mpa
Processing temperature180-230°C °C
Screw speed- rpm
thermal performanceTest ConditionTest MethodTAIWAN CHIMEI/PA-717C
Combustibility (rate)UL 941.6mmHB
Hot deformation temperatureHDTASTM D648/ISO 7587(189) ℃（℉）
Linear coefficient of thermal expansionASTM D696/ISO 11359- mm/mm.℃
Vicat softening temperatureASTM D1525/ISO R306104(219) ℃（℉）
mechanical propertiesTest ConditionTest MethodTAIWAN CHIMEI/PA-717C
Bending modulusASTM D790/ISO 17825000(35000) kg/cm²(MPa)[Lb/in²]
bending strengthASTM D790/ISO 178720(10.200) kg/cm²(MPa)[Lb/in²]
Charpy Notched Impact StrengthASTM D256/ISO 179- kg·cm/cm(J/M)ft·lb/in
elongationASTM D638/ISO 52715 %
Elongation at BreakASTM D638/ISO 527- %
Impact strength of cantilever beam gapASTM D256/ISO 17928(5.2) kg·cm/cm(J/M)ft·lb/in
Rockwell hardnessASTM D785R-115
Tensile modulusASTM D638/ISO 527- kg/cm²(MPa)[Lb/in²]
tensile strengthASTM D638/ISO 527450(6.380) kg/cm²(MPa)[Lb/in²]
otherTest ConditionTest MethodTAIWAN CHIMEI/PA-717C
characteristic高冲击强度
Color-
purpose厨房用具 / 音响用品 / 马桶盖 / 洗衣机 / 吸尘器外壳 / 工具手柄配件等
remarks符合UL及八大重金属等检验之规范
Physical propertiesTest ConditionTest MethodTAIWAN CHIMEI/PA-717C
densityASTM D792/ISO 11831.04
melt mass-flow rateASTM D1238/ISO 113314 g/10min
Shrinkage rateASTM D955- %
Water absorption rateASTM D570/ISO 62- %