ABS ABS A100-36 Chase Plastics Services Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Chase Plastics Services Inc./ABS A100-36 |
---|---|---|---|
Impact strength of cantilever beam gap | -30°C,6.35mm | ASTM D256 | 130 J/m |
23°C,6.35mm | ASTM D256 | 340 J/m | |
23°C,3.18mm | ASTM D256 | 390 J/m |
hardness | Test Condition | Test Method | Chase Plastics Services Inc./ABS A100-36 |
---|---|---|---|
Rockwell hardness | R级 | ASTM D785 | 108 |
Mechanical properties | Test Condition | Test Method | Chase Plastics Services Inc./ABS A100-36 |
---|---|---|---|
elongation | 断裂,3.20mm | ASTM D638 | 40 % |
bending strength | 3.20mm | ASTM D790 | 72.6 MPa |
Tensile modulus | 3.20mm | ASTM D638 | 2080 MPa |
Flexural modulus | 3.20mm | ASTM D790 | 2450 MPa |
tensile strength | 屈服,3.20mm | ASTM D638 | 45.1 MPa |
physical property | Test Condition | Test Method | Chase Plastics Services Inc./ABS A100-36 |
---|---|---|---|
Shrinkage rate | MD:3.20mm | ASTM D955 | 0.40to0.70 % |
density | ASTM D792 | 1.04 g/cm³ | |
melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 21 g/10min |
Thermal performance | Test Condition | Test Method | Chase Plastics Services Inc./ABS A100-36 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,6.40mm,HDT | ASTM D648 | 87.0 °C |
vicat | ASTM D15255 | 93.0 °C | |
Heat distortion temperature | 0.45MPa,未退火,6.40mm,HDT | ASTM D648 | 91.0 °C |