Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PC ML6411-GY6E517 SABIC INNOVATIVE NANSHA

LEXAN™

Electrical appliances,Architectural Applications,Plastic bag,Lighting applications

Easy to form,Short molding cycle,Low temperature and high

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/ML6411-GY6E517
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	114 °C
		0.45 MPa, Unannealed, 4.00 mm, 100 mm Span8	ISO 75-2/Be	125 °C
		1.8 MPa, Unannealed, 4.00 mm, 100 mm Span8	ISO 75-2/Ae	115 °C
		0.45 MPa, Unannealed, 6.40 mm	ASTM D648	128 °C
		1.8 MPa, Unannealed, 6.40 mm	ASTM D648	119 °C
Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	7.0E-5 cm/cm/°C
		Flow : -40 to 40°C	ASTM E831	7.7E-5 cm/cm/°C
		Flow : -40 to 40°C	ISO 11359-2	7.0E-5 cm/cm/°C
		Across Flow : -40 to 40°C	ASTM E831	5.9E-5 cm/cm/°C
RTI		UL 746	100 °C
RTI Elec		UL 746	100 °C
RTI Imp		UL 746	100 °C
Vicat softening temperature	--	ISO 306/B120	135 °C
Vicat softening temperature		--	ASTM D15259	134 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/ML6411-GY6E517
Bending modulus	--5	ISO 178	2350 Mpa
Bending modulus		50.0 mm Span4	ASTM D790	2600 Mpa
bending strength	Yield, 50.0 mm Span4	ASTM D790	95.0 Mpa
bending strength		--5,6	ISO 178	90.0 Mpa
elongation	Yield	ISO 527-2/50	5.0 %
		Yield3	ASTM D638	5.0 %
		Break3	ASTM D638	100 %
		Break	ISO 527-2/50	100 %
Tensile modulus	--2	ASTM D638	2500 Mpa
Tensile modulus		--	ISO 527-2/1	2350 Mpa
tensile strength	Yield	ISO 527-2/50	62.0 Mpa
		Break	ISO 527-2/50	58.0 Mpa
		Break3	ASTM D638	54.0 Mpa
		Yield3	ASTM D638	62.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/ML6411-GY6E517
Compared to the anti leakage trace index		UL 746	PLC 2
Compared to the anti leakage trace index			IEC 60112	V
Dielectric strength	3.20 mm, in Oil	ASTM D149	27 KV/mm
High arc combustion index		UL 746	PLC 1
Hot wire ignition		UL 746	PLC 3
Volume resistivity		IEC 60093	> 1.0E+15 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/ML6411-GY6E517
melt mass-flow rate	260°C/2.16 kg	ASTM D1238	7.0 g/10 min
Melt Volume Flow Rate (MVR)	260°C/5.0 kg	ISO 1133	18.0 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.40 - 0.80 %
Water absorption rate	Saturation, 23°C	ISO 62	0.30 %
Water absorption rate		Equilibrium, 23°C, 50% RH	ISO 62	0.10 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/ML6411-GY6E517
Dart impact	23°C, Total Energy	ASTM D3763	72.0 J

flammability	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/ML6411-GY6E517
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	2.0 mm	IEC 60695-2-13	800 °C
		3.0 mm	IEC 60695-2-13	800 °C
		1.0 mm	IEC 60695-2-13	800 °C
UL flame retardant rating	3.0 mm	UL 94	5VA
		2.0 mm	UL 94	5VB
		1.5 mm	UL 94	V-0

injection	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/ML6411-GY6E517
drying temperature			90 to 100 °C
drying time			2.0 to 4.0 hr
Hopper temperature			60 to 80 °C
Mold temperature			60 to 90 °C
Processing (melt) temperature			270 to 300 °C
Spray nozzle temperature			250 to 290 °C
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			260 to 300 °C
Temperature at the rear of the barrel			230 to 260 °C
Temperature in the middle of the barrel			250 to 290 °C