Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
MVLDPE 183 SK KOREA
NEXLENE®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | SK KOREA/183 |
|---|---|---|---|
| tensile strength | TD : 断裂, 25 µm | ASTM D882 | 39.2 Mpa |
| elongation | MD : 断裂, 25 µm | ASTM D882 | 450 % |
| Elmondov tear strength | TD : 25 µm | ASTM D1922 | 21 g |
| Secant modulus | 1% 正割, TD : 25 µm | ASTM D882 | 132 Mpa |
| 1% 正割, MD : 25 µm | ASTM D882 | 112 Mpa | |
| elongation | TD : 断裂, 25 µm | ASTM D882 | 700 % |
| tensile strength | MD : 断裂, 25 µm | ASTM D882 | 49.0 Mpa |
| Elmondov tear strength | MD : 25 µm | ASTM D1922 | 10 g |
| Film thickness - tested | ASTM D374 | 25 µm | |
| Falling hammer impact | 25 µm | ASTM D1709A | 270 g |
| optical performance | Test Condition | Test Method | SK KOREA/183 |
|---|---|---|---|
| Sealing Initial Temperature | 内部方法 | 105 °C | |
| Haze ratio | ASTM D1003 | 1.5 % |
| squeeze out | Test Condition | Test Method | SK KOREA/183 |
|---|---|---|---|
| Melt Temperature | 230 °C |
| physical property | Test Condition | Test Method | SK KOREA/183 |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16 kg | ASTM D1238 | 3.0 g/10 min |
| Thermal performance | Test Condition | Test Method | SK KOREA/183 |
|---|---|---|---|
| vicat | ASTM D1525 | 105 °C | |
| melting temperature | 内部方法 | 115 °C |