HDPE F0554T SUMITOMO JAPAN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | SUMITOMO JAPAN/F0554T |
|---|---|---|---|
| tensile strength | 断裂2 | ASTMD882 | 55.0 Mpa |
| Falling hammer impact | --2 | ASTMD1709 | 250 g |
| Secant modulus -1% Decant, TD | --2 | ASTMD882 | 1140 Mpa |
| Falling hammer impact | --3 | ASTMD1709 | 330 g |
| Secant modulus -1% Decant, TD | --3 | ASTMD882 | 1030 Mpa |
| ElmendorfTearStrength-TD | --3 | ASTMD1922 | 39 g |
| elongation | 断裂3 | ASTMD882 | 560 % |
| ElmendorfTearStrength-TD | --2 | ASTMD1922 | 78 g |
| tensile strength | 断裂3 | ASTMD882 | 70.0 Mpa |
| Secant modulus -1% Decant, MD | --3 | ASTMD882 | 930 Mpa |
| tensile strength | 断裂2 | ASTMD882 | 75.0 Mpa |
| elongation | 断裂2 | ASTMD882 | 520 % |
| Secant modulus -1% Decant, MD | --2 | ASTMD882 | 990 Mpa |
| tensile strength | 屈服 | ASTMD882 | 35.0 Mpa |
| tensile strength | 屈服 | ASTMD882 | 30.0 Mpa |
| Elmondov tear strength MD | --2 | ASTMD1922 | 11 g |
| --3 | ASTMD1922 | 17 g | |
| tensile strength | 断裂3 | ASTMD882 | 65.0 Mpa |
| Tensile strain | 断裂3 | ASTMD882 | 550 % |
| 断裂2 | ASTMD882 | 560 % |
| physical property | Test Condition | Test Method | SUMITOMO JAPAN/F0554T |
|---|---|---|---|
| melt mass-flow rate | 190°C/21.6kg | ASTMD1238 | 9.3 g/10min |
| 190°C/2.16kg | ASTMD1238 | 0.050 g/10min |
| Thermal performance | Test Condition | Test Method | SUMITOMO JAPAN/F0554T |
|---|---|---|---|
| vicat | ASTMD15254 | 126 °C |