PC 141R-111 SABIC INNOVATIVE JAPAN
LEXAN™
--
transparent、Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/141R-111 |
|---|---|---|---|
| Izod Notched at 23 ℃ (73 ℉) | ASTM D256 | 801 J/m | |
| / | ASTM D3763 | 63 J | |
| Cantilever beam without notch (Izod Unnotched) 23 ℃ (73 ℉) | / | ASTM D4812 | 3204 J/m |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/141R-111 |
|---|---|---|---|
| Rockwell hardness R | ASTM D 785 | 118 R | |
| ASTM D 785 | 70 M |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/141R-111 |
|---|---|---|---|
| Tensile strength fracture (brk) | Type I, 5 | ASTM D638 | 68 Mpa |
| Flexural modulus | 1.3 mm/ | ASTM D790 | 2340 Mpa |
| Tensile strength yield (yld) | Type I, 5 | ASTM D638 | 62 Mpa |
| Type I, 5 | ASTM D638 | 130 % | |
| 1.3 mm/min/ | ASTM D790 | 96 Mpa |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/141R-111 |
|---|---|---|---|
| transmittance | 2.54 mm | ASTM D1003 | 88 % |
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/141R-111 |
|---|---|---|---|
| Vicat softening temperature | Rate B/50 | ASTM D1525 | 154 °C |
| Relative Temperature Index (RTI) intensity w/o impact- | UL 746B | 130 °C | |
| Relative Temperature Index (RTI) impact w/impact- | UL 746B | 130 °C | |
| Relative Temperature Index (RTI) Electrical Elec- | UL 746B | 130 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/141R-111 |
|---|---|---|---|
| Water absorption rate | 24 hours | ASTM D570 | 0.15 |
| Melt Mass Flow Rate (MFR) 300 ℃/1.2 kg | / | ASTM D1238 | 10.5 g/10min |
| Water absorption rate | equilibriu | ASTM D570 | 0.35 |
| Longitudinal shrinkage rate (Flow) | flow, 3.2 | Internal | 0.5~0.7 |
| specific volume | / | ASTM D792 | 0.83 |