PC EXL9330 BK1A068 SABIC INNOVATIVE US
LEXAN™ 
food,Thin walled products,Casters
UV resistance,Toughening,Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodSABIC INNOVATIVE US/EXL9330 BK1A068
Ball Pressure TestH 358/30ISO 2039-190.0 Mpa
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL9330 BK1A068
Ball Pressure Test123 到 127°CIEC 60695-10-2通过
Hot deformation temperature0.45 MPa, 未退火, 3.20 mmASTM D648134 °C
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距11ISO 75-2/Ae124 °C
1.8 MPa, 未退火, 6.40 mmASTM D648124 °C
0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距11ISO 75-2/Be135 °C
1.8 MPa, 未退火, 3.20 mmASTM D648120 °C
Linear coefficient of thermal expansion横向 : -40 到 40°CASTM E8316.7E-5 cm/cm/°C
流动 : -40 到 40°CASTM E8316.7E-5 cm/cm/°C
横向 : 23 到 80°CISO 11359-27.7E-5 cm/cm/°C
流动 : 23 到 80°CISO 11359-27.2E-5 cm/cm/°C
RTIUL 746125 °C
RTI ElecUL 746125 °C
RTI ImpUL 746115 °C
Vicat softening temperature--ASTM D152512142 °C
--ISO 306/B50140 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL9330 BK1A068
Bending modulus--5ISO 1782200 Mpa
50.0 mm 跨距4ASTM D7902060 Mpa
bending strength屈服, 50.0 mm 跨距4ASTM D79088.0 Mpa
--5,6ISO 17885.0 Mpa
elongation屈服ISO 527-2/506.0 %
屈服3ASTM D6386.0 %
断裂3ASTM D638130 %
断裂ISO 527-2/50130 %
Tensile modulus--2ASTM D6382100 Mpa
--ISO 527-2/12100 Mpa
tensile strength断裂ISO 527-2/5060.0 Mpa
断裂3ASTM D63861.0 Mpa
屈服ISO 527-2/5055.0 Mpa
屈服3ASTM D63858.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL9330 BK1A068
Compared to the anti leakage trace indexUL 746PLC 3
IEC 60112PLC 3
Dielectric constant50 HzIEC 602502.60
50 kHzASTM D1502.95
60 HzASTM D1502.95
1 MHzIEC 602502.70
1 MHzASTM D1502.90
60 HzIEC 602502.60
Dielectric strength3.20 mm, in OilASTM D14917 KV/mm
3.20 mm, 在油中IEC 60243-116 KV/mm
Dissipation factor1 MHzASTM D1508.5E-3
60 HzASTM D1502.4E-3
50 HzIEC 602501.0E-3
60 HzIEC 602501.0E-3
50 HzASTM D1502.4E-3
High arc combustion indexUL 746PLC 0
Hot wire ignitionUL 746PLC 1
Surface resistivityIEC 60093> 1.0E+15 ohms
Volume resistivityIEC 60093> 1.0E+15 ohms·cm
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL9330 BK1A068
density--ISO 11831.19 g/cm³
--ASTM D7921.18 g/cm³
melt mass-flow rate300°C/1.2 kgASTM D123810 g/10 min
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 11339.00 cm3/10min
Outdoor applicabilityUL 746Cf1
Shrinkage rate流动 : 3.20 mmInternal Method0.40 - 0.80 %
横向流动 : 3.20 mmInternal Method0.40 - 0.80 %
Water absorption rate饱和, 23°CISO 620.35 %
平衡, 23°C, 50% RHISO 620.15 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL9330 BK1A068
Charpy Notched Impact Strength23°CISO 179/1eA75 kJ/m²
-30°CISO 179/1eA60 kJ/m²
Dart impact23°C, Total EnergyASTM D376352.0 J
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
23°CISO 180/1U无断裂
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/EXL9330 BK1A068
Burning wire flammability index1.0 mmIEC 60695-2-12960 °C
Extreme Oxygen IndexISO 4589-235 %
Hot filament ignition temperature1.0 mmIEC 60695-2-13825 °C
UL flame retardant rating3.0 mmUL 945VA
1.5 mmUL 94V-0
injectionTest ConditionTest MethodSABIC INNOVATIVE US/EXL9330 BK1A068
Back pressure0.300 to 0.700 Mpa
drying temperature120 °C
drying time3.0 to 4.0 hr
Exhaust hole depth0.025 to 0.076 mm
Mold temperature70 to 95 °C
Processing (melt) temperature295 to 315 °C
Screw speed40 to 70 rpm
Spray nozzle temperature290 to 310 °C
Suggested injection volume40 to 60 %
Suggested maximum moisture content0.020 %
Temperature at the front of the material cylinder295 to 315 °C
Temperature at the rear of the barrel215 to 295 °C
Temperature in the middle of the barrel280 to 305 °C