Ionomer FORMION® FI 200HFU A SCHULMAN USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | A SCHULMAN USA/FORMION® FI 200HFU |
|---|---|---|---|
| Impact strength of cantilever beam gap | 22°C,3.20mm | ASTM D256A | NoBreak |
| Multi-AxialInstrumentedImpactEnergy | 3.20mm,InjectionMolded,DuctileFailure | ISO 6603-2 | 45.0 J |
| hardness | Test Condition | Test Method | A SCHULMAN USA/FORMION® FI 200HFU |
|---|---|---|---|
| Rockwell hardness | R-Scale,22°C,3.20mm | ASTM D785 | 95 |
| Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/FORMION® FI 200HFU |
|---|---|---|---|
| Tensile strain | Break,21°C,4.00mm,InjectionMolded | ASTM D638 | 250 % |
| tensile strength | Yield,22°C,3.20mm,InjectionMolded | ASTM D638 | 45.0 MPa |
| Flexural modulus | 22°C,3.20mm,InjectionMolded,50.0mmSpan，正切 | ASTM D790A | 1000 MPa |
| physical property | Test Condition | Test Method | A SCHULMAN USA/FORMION® FI 200HFU |
|---|---|---|---|
| Shrinkage rate | MD：72hr,3.20mm | ASTM D955 | 0.80to1.0 % |
| density | ASTM D792A | 1.04 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 16 g/10min |
| Thermal performance | Test Condition | Test Method | A SCHULMAN USA/FORMION® FI 200HFU |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.20mm,注塑，HDT | ASTM D648A | 65.0 °C |