PA66 1402SH XA1 PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PA66 ASAHI JAPAN 1402SH XA1

Injection grade

US$ 3,280 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	ASAHI JAPAN/1402SH XA1
elongation	Break	ASTM D638	50 %
Taber abraser	1000Cycles	ASTM D1044	-- mg
tensile strength	Yield,23°C	ISO 527-2	82.0 Mpa
Tensile strain	Yield,23°C	ISO 527-2	4.5 %
Rockwell hardness	干(湿)	ASTM D-785	80(55) R scale
bending strength	23°C	ISO 178	111 Mpa
bending strength		干(湿)	ASTM D-790	118(50) Mpa
tensile strength		ASTM D638	79.0 Mpa
bending strength		ASTM D790	118 Mpa
tensile strength	干(湿)	ASTM D-638	79(55) Mpa
flexural coefficient	干(湿)	ASTM D-790	2.8(1.0) GPa
Impact strength of cantilever beam gap	干(湿)	ASTM D-256	39(196) J/m
Bending modulus	23°C	ISO 178	2600 Mpa
Bending modulus			ASTM D790	2800 Mpa
Elongation at Break	干(湿)	ASTM D-638	50(270) %
Tensile modulus	23°C	ISO 527-2	3000 Mpa
Tensile strain	Break,23°C	ISO 527-2	-- %
flammability	Test Condition	Test Method	ASAHI JAPAN/1402SH XA1
UL flame retardant rating	0.75mm	UL 94	V-2
Extreme Oxygen Index		ASTM D2863	26 %
thermal performance	Test Condition	Test Method	ASAHI JAPAN/1402SH XA1
Hot deformation temperature	0.46MPa,干	ASTM D-648	230 °C
Hot deformation temperature		1.82MPa,干	ASTM D-648	70 °C
specific heat			1670 J/kg/°C
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	230 °C
Linear coefficient of thermal expansion	MD	ASTM D696	8E-05 cm/cm/°C
thermal conductivity	干		0.2 W/(m.K)
Linear coefficient of thermal expansion	干	ASTM D-696	8
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	162 °C
UL flame retardant rating	干	UL 94	V-2
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	70.0 °C
thermal conductivity			0.20 W/m/K
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	62.0 °C
specific heat	干		1670 J/(kg.k)
Physical properties	Test Condition	Test Method	ASAHI JAPAN/1402SH XA1
Wear factor	湿	ASTM D-1044	7
Shrinkage rate	干	旭化成方法	1.3-2.0 %
Shrinkage rate		MD	Internal Method	1.3-2.0 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	-- %
Water absorption rate		Saturation,23°C		-- %
hardness	Test Condition	Test Method	ASAHI JAPAN/1402SH XA1
Rockwell hardness	M-Sale	ASTM D785	80
		M-Sale	ISO 2039-2	80
		R-Sale	ASTM D785	120
		R-Sale	ISO 2039-2	120
Electrical performance	Test Condition	Test Method	ASAHI JAPAN/1402SH XA1
Volume resistivity	23°C	IEC 60093	1E+14 ohms·cm
Compared to the anti leakage trace index	3.00mm	IEC 60112	PLC 1
Surface resistivity		IEC 60093	1E+13 ohms
Dielectric strength		IEC 60243-1	20 KV/mm
Basic Performance	Test Condition	Test Method	ASAHI JAPAN/1402SH XA1
Water absorption rate	湿		2.5 %
impact performance	Test Condition	Test Method	ASAHI JAPAN/1402SH XA1
Impact strength of simply supported beam without notch		ISO 179	NoBreak
Other performance	Test Condition	Test Method	ASAHI JAPAN/1402SH XA1
Extreme Oxygen Index	干	ASTM D-2863	26 %