PPS FZ-2100 E1035 DIC JAPAN
DIC.PPS 
--
Ductility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodDIC JAPAN/FZ-2100 E1035
Rockwell hardnessASTM D785100 M(Scale)
ASTM D785121 R
Mechanical propertiesTest ConditionTest MethodDIC JAPAN/FZ-2100 E1035
Impact strength of cantilever beam gap23°CASTM D25640 J/m
coefficient of friction静态ASTM D37020.35
bending strength23°CASTM D790130 Mpa
Tensile modulus23°CASTM D6384200 Mpa
elongation at break23°CASTM D638>15 %
coefficient of friction动态ASTM D37020.40
Tensile modulus泊松比7.58 0.38
Flexural modulus23°CASTM D7903800 Mpa
tensile strength 23°CASTM D63880 Mpa
Electrical performanceTest ConditionTest MethodDIC JAPAN/FZ-2100 E1035
Dissipation Factor耐电弧性ASTM D495125 S
23°CASTM D1502E-03 1MHz
Volume resistivityASTM D2571E+16 Ω.cm
dielectric strength1.60mmASTM D14923 KV/mm
dielectric constant23°CASTM D1503.3 1MHz
Dissipation Factor相对漏电起痕指数ASTM D3638135 V
Flame retardant performanceTest ConditionTest MethodDIC JAPAN/FZ-2100 E1035
UL flame retardant ratingUL -94V-0 0.75mm
physical property Test ConditionTest MethodDIC JAPAN/FZ-2100 E1035
Shrinkage rateMDASTM D9951.30 %
Water absorption rate(23°C,24hr)ASTM D5700.02 %
Shrinkage rateTDASTM D9951.50 %
Thermal performanceTest ConditionTest MethodDIC JAPAN/FZ-2100 E1035
Linear coefficient of thermal expansionTDASTM D6964E-05 cm/cm/°C
Heat distortion temperature1.80MPa未退火,HDTASTM D648110 °C
Linear coefficient of thermal expansionMDASTM D6964E-05 cm/cm/°C
Heat distortion temperature0.45MPa未退火,HDTASTM D648200 °C