Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS H605 INEOS USA
Novodur® 
Automotive sector、Application in the automo、Automotive interior equip
heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodINEOS USA/H605
Impact strength of cantilever beam gap-30°CISO180/A7.0 kJ/m²
23°CISO180/A17 kJ/m²
Charpy Notched Impact Strength-30°CISO1797.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO17990 kJ/m²
-30°CISO17980 kJ/m²
Charpy Notched Impact Strength23°CISO17917 kJ/m²
hardnessTest ConditionTest MethodINEOS USA/H605
ISO2039-1105 Mpa
Mechanical propertiesTest ConditionTest MethodINEOS USA/H605
Tensile strain屈服,23°CISO527-22.5 %
Bending stressISO17872.0 Mpa
Tensile modulusISO527-22400 Mpa
Tensile stress屈服,23°CISO527-247.0 Mpa
Flexural modulusISO1782400 Mpa
Tensile strain断裂,23°CISO527-2>15 %
Electrical performanceTest ConditionTest MethodINEOS USA/H605
Dissipation Factor1MHzIEC602508E-03
CTIIEC60112600 V
1MHzIEC602503.00
dielectric strength1.50mmIEC60243-133 KV/mm
100HzIEC602503.10
Dissipation Factor100HzIEC602505E-03
physical property Test ConditionTest MethodINEOS USA/H605
densityISO11831.05 g/cm³
Melt volume flow rate220°C/10.0kgISO113325.0 cm3/10min
Shrinkage rateISO294-40.40到0.60 %
Thermal performanceTest ConditionTest MethodINEOS USA/H605
vicatISO306/B50101 °C
Hot deformation temperature 31.8MPa,退火ISO75-2/A98.0 °C
MDISO11359-28E-05 cm/cm/°C
Hot deformation temperature 30.45MPa,退火ISO75-2/B102 °C