PC CLS400 MITSUBISHI THAILAND
IUPILON™ 
Automotive Applications、electrical equipment、glasses、lens
Thermal stability、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI THAILAND/CLS400
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Electrical performanceTest ConditionTest MethodMITSUBISHI THAILAND/CLS400
dielectric strength1.00mmIEC 60243-131 KV/mm
Volume resistivityIEC 600933E+16 ohms·cm
relative permittivity100HzIEC 602503.10
Dissipation Factor100HzIEC 602506E-04
dielectric strength3.00mmIEC 60243-118 KV/mm
relative permittivity1MHzIEC 602503.10
Surface ResistivityIEC 600936E+15 ohms
Dissipation Factor1MHzIEC 602509E-03
Mechanical propertiesTest ConditionTest MethodMITSUBISHI THAILAND/CLS400
Tensile modulusISO 527-22400 Mpa
Nominal tensile fracture strainISO 527-2110 %
bending strengthISO 17893.0 Mpa
Flexural modulusISO 1782300 Mpa
Tensile strain屈服ISO 527-25.5 %
tensile strength 屈服ISO 527-260.0 Mpa
physical property Test ConditionTest MethodMITSUBISHI THAILAND/CLS400
Shrinkage rateTD:3.20mm0.50-0.70 %
Melt volume flow rate300°C/1.2kgISO 11337.50 cm3/10min
Shrinkage rateMD:3.20mm0.50-0.70 %
Water absorption rate饱和,23°CISO 620.24 %
melt mass-flow rate300°C/1.2kgISO 11338.0 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI THAILAND/CLS400
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B145 °C
1.8MPa,未退火，HDTISO 75-2/A131 °C
Linear coefficient of thermal expansionMDISO 11359-26.5E-05 cm/cm/°C
TDISO 11359-26.6E-05 cm/cm/°C