ABS 1001 FR VO/4 ROMIRA GERMANY
ROTEC®
--
Filler: Glass beads、20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ROMIRA GERMANY/1001 FR VO/4 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 70 kJ/m² |
| Mechanical properties | Test Condition | Test Method | ROMIRA GERMANY/1001 FR VO/4 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 65.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2600 Mpa |
| Tensile modulus | 23°C | ISO 527-2/1 | 2800 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2/50 | 10 % |
| tensile strength | 23°C | ISO 527-2/50 | 42.0 Mpa |
| flammability | Test Condition | Test Method | ROMIRA GERMANY/1001 FR VO/4 |
|---|---|---|---|
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 700 °C |
| 1.5mm | IEC 60695-2-13 | 750 °C | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 850 °C |
| physical property | Test Condition | Test Method | ROMIRA GERMANY/1001 FR VO/4 |
|---|---|---|---|
| Shrinkage rate | 23°C | ISO 294-4 | 0.30-0.60 % |
| density | 23°C | ISO 1183 | 1.20 g/cm³ |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.30 % |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 64 g/10min |
| Thermal performance | Test Condition | Test Method | ROMIRA GERMANY/1001 FR VO/4 |
|---|---|---|---|
| Ball indentation test | 75°C,3.00mm | IEC 60695-10-2 | <2.00 mm |
| vicat | ISO 306/B50 | 86.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 75.0 °C |